Muundo wa Kemikali:
Muundo wa kemikali wa bomba la chuma cha pua 2205
| Cr | Ni | Mo | Co | Nb (+Ta) | Ti | V | W | Cu | C | Mn | N | Si | P | S | Fe | Al | |
| Dak | 22.00 | 4.50 | 3.00 | 0.14 | 0.20 | ||||||||||||
| Max | 23.00 | 6.50 | 3.50 | 0.03 | 0.20 | 0.70 | 0.03 | 0.02 | Bal |
Sifa za Mitambo:
Muundo wa kemikali wa bomba la chuma cha pua 2205
| Mfadhaiko wa 0.2%. | 450 N/mm2 | 65ksi |
| Nguvu ya Mkazo | 655 N/mm2 | 95ksi |
| Kurefusha, 5.65√S0 | 25% | |
| Kupunguza eneo | 45% | |
| Ugumu (Brinell) | <270 | |
| Nguvu ya Athari (Joto la Chumba) | 80J (av) | |
| Nguvu ya Athari (-46°C) : Longitudinal | <100mm 80J | |
| 100-260mm 45J (dakika 35J) | ||
| >260mm Kwa maelezo pekee | ||
| Nguvu ya Athari (-46oC): Kuvuka | 50-260mm 45J (dakika 35J) | |
| >260mm Kwa maelezo pekee | ||
Vidokezo:
Muundo wa kemikali wa bomba la chuma cha pua 2205
- Upimaji utafanywa kwa mujibu wa ASTM A370 au EN ISO 6892-1 (tensile), EN ISO 6506-1 (ugumu)
- Kiwango cha chini cha mali kilichonukuliwa (kilichojaribiwa kwa joto la kawaida katika mwelekeo wa longitudinal)
- Upimaji uliofanywa kwa kila kuyeyuka kwa nyenzo kwa kundi la matibabu ya joto
- Ugumu utakuwa kwa mujibu wa NACE MR 1075
- Jaribio la kutu la ASTM G48A (kwa 25°C) Hakuna shimo na chini ya 3.0g/m2kupungua uzito
- Maudhui ya ferrite 40-55%
- Muundo mdogo umeidhinishwa bila kabidi za mipaka ya nafaka, awamu za sigma, chi na laves
Sifa za Kimwili: muundo wa kemikali wa bomba la chuma cha pua 2205
| Msongamano (Kg/m3) | 7810 |
| Upenyezaji wa Sumaku (20°C) | <50 |
| Moduli ya Vijana (kN/mm2) | 190 |
| Ustahimilivu Mahususi wa Umeme, 20°C (µΩ.m) | 0.85 |
| Wastani wa mgawo wa upanuzi wa joto, 20-300°C (m/m/oC) | 11 x 10-6 |
| Joto Maalum, 20°C (J/kg.K) | 400 |
| Uendeshaji wa joto, 20°C (W/mK) |